1.4372 vs 1.4301 stainless steel: what's the difference?
Tinggalkan pesan
When choosing stainless steel materials, 1.4372 stainless steel and 1.4301 stainless steel (AISI 304) are often compared. They are both austenitic stainless steels, but there are obvious differences in chemical composition, corrosion resistance, mechanical properties, magnetism and price. This article will take you to an in-depth understanding of the key differences between 1.4372 and 1.4301, helping you make a more appropriate choice based on your actual needs.
1.4372 vs 1.4301 stainless steel: Chemical Composition (Major Elements, %)
| 1.4372 (X12CrMnNiN17-7-5) | 1.4301 (X5CrNi18-10) | |
|---|---|---|
| Less than or equal to 0.15 | Less than or equal to 0.07 | |
| 16.0–18.0 | 17.5–19.5 | |
| 3.5–5.5 | 8.0–10.5 | |
| 5.5–7.5 | Less than or equal to 2.0 | |
| 0.05–0.25 | Less than or equal to 0.11 (typically trace) |
1.4372 vs 1.4301 stainless steel: Mechanical Properties
| 1.4372 | 1.4301 | |
|---|---|---|
| Greater than or equal to 635 MPa (higher strength) | Greater than or equal to 520 MPa (moderate strength) | |
| Greater than or equal to 245 MPa (Mn/N strengthening) | Greater than or equal to 215 MPa | |
| Greater than or equal to 40% (good ductility) | Greater than or equal to 40% (excellent ductility) | |
| Typically Less than or equal to 217 HBW | Typically Less than or equal to 187 HBW |
1.4372 vs 1.4301 stainless steel: Physical Properties
| 1.4372 | 1.4301 | |
|---|---|---|
| 7.93 g/cm³ | 7.93 g/cm³ | |
| ~16 W/(m·K) | ~16.2 W/(m·K) | |
| 17.3×10⁻⁶/ degree | 17.2×10⁻⁶/ degree | |
| Non-magnetic (austenitic) | Non-magnetic (austenitic) |
Which one is better in corrosion resistance, 1.4301 or 1.4372 stainless steel?
1.4301's high nickel-chromium (Cr17.5–19.5%, Ni8–10.5%) forms a more stable passivation film, which is more resistant to chloride ions (such as seawater and salt spray), and is suitable for humid or corrosive environments.
High temperature oxidation: 1.4301 can be used for a long time at Less than or equal to 800 degree , and 1.4372 is only suitable for Less than or equal to 600 degree .
Price per kilogram of 1.4301 stainless steel?
1.4372: Due to its low nickel content (about 50% of 1.4301), the cost is significantly lower, and it is suitable for non-critical parts that do not require high corrosion resistance (such as ordinary structural parts, low-cost decoration).
1.4301: It has balanced comprehensive performance and is the "panacea" among stainless steels. Although the price is higher, it is more cost-effective in corrosive environments and has a long
Are 1.4372 and 1.4301 stainless steels magnetic?
Both are austenitic stainless steels and are non-magnetic at room temperature (unless cold worked to martensitic transformation, they may be weakly magnetic).